  • Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

  • This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

  • The above are the three major advantages of the positive and negative twisting barbed wire, mainly including durability, high cost performance, and beautiful appearance.


  • Post time: 12-05-23

  • Post time: 17-05-22
  • Electrically

  • In use, there is no need for daily maintenance and maintenance, not only can save a lot of time, but also can reduce costs, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different types, can choose according to their own needs. With good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, in the production of annealing wire is made of steel wire, now more used in the construction industry binding use, compared with ordinary wire is also more soft, have better luster.

  • Fence use: generally used as a fence is a plastic-impregnated welded wire mesh with a height of 1.2 meters to 2 meters. Most of the mesh holes are 6cm, and the wire diameter varies from 2mm to 3mm.

  • The whole country is cooling down on a massive scale. People suddenly feel that winter is coming. In much of the north, the collection of central heating and heating has also begun. People who do not have central heating or do not want to use traditional heating choose air heating. As heating equipment enters the peak season, building network sales are also gradually increasing.

  • galvanized

  • Wire rod to stop normalizing or soxaustenitizing treatment, large specifications with spheroidizing annealing instead. In the middle, especially before the waste product drawing process of thermal disposal throughout the selection of soxaustenitizing disposal. Decarbonization should be prevented during thermal disposal. Sulfuric acid or hydrochloric acid pickling was used to remove the oxide sheet after hot treatment. Coating (see lubrication carrier) can be dipped in lime, phosphating, borax disposal or copper plating.
  • Hexagonal hulanwang custom applications in the channel slope protection work plays a very important role, according to the network performance, it can make is not firmly grasp soil erosion, so hexagonal hulanwang custom slope protection effect is very significant, but also because of this advantage, is widely used in such as channel protection, river bank protection, protection of landslides.
  • iron

  • The shape of the cage has round, square, octagonal, hexagonal and other shapes. Because the circular space uses a large area, it is more suitable for the activities of birds, and it is not easy to get hurt, so it is popular with everyone. A cage is dear to a man who loves birds, for it is inhabited by his master’s birds. If well maintained, it can be maintained for many years. Let’s look at how to maintain the cage.

  • 5, according to the wire diameter thickness to adjust zinc dipping time

  • Hongyu twist flower hexagonal mesh factory is the selection of low carbon steel silk woven, mesh structure he has the characteristics of corrosion resistance, high strength and ductility. Steel wire diameter up to 2.0mm-4.0mm, steel wire appearance is usually selected hot dip galvanized maintenance, galvanized maintenance layer thickness can be made according to customer needs, galvanized maximum can reach 300g/㎡.

  • 1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

  • Cattle net in outdoor use for a long time will inevitably show rust corrosion, this time the use of cattle net life depends on the maintenance of the product is not in place, we all know cattle net if a long time exposure to the harsh environment, the service life will be greatly reduced. How long does a normal cattle net last?

  • Railroad

  • hook

  • 1. Zinc pot operators must stick to their posts

  • Barbed rope used to enclose cattle, sheep and other livestock is also the biggest characteristic of low price, for users engaged in breeding industry, the investment is not small, the use of barbed rope fence on the one hand is to reduce the cost, on the other hand, is better protection effect.

  • 3. The structure of the dog cage should be reasonable
  • Magnetic test method is the original common difference between austenitic stainless steel and ferritic stainless steel simple way, austenitic stainless steel is wrong magnetic steel, but after cold processing under large pressure will have a slight magnetic; But pure chrome steel and low alloy steel are strong magnetic steel.

  • The guide frame of spray hook net wholesale is composed of guide beam and park core pile, their interval distance is about 3 meters, the spacing of guide beam should be about 1 cm higher than the wall. When installing the guide beam, its position should be far away from the net, and the surround-pile should not be expanded, which will make the surround-pile sink or change its shape.

  • Hexagonal mesh is a metal wire woven Angle mesh (hexagonal) made of wire mesh, the use of metal wire diameter is based on the size of the hexagonal and different. Also known as: twist flower net, stone cage net, gabion net, flood control network.

  • Three is to do a good job of galvanized silk product production site clean and tidy, in accordance with the scientific method of operation to operate the production, the operator should wear the required dress. If it is hot dip galvanized wire products, we must do a good job of passivation treatment, will be able to effectively prevent discoloration, prolong the method of discoloration, can solve the problem of discoloration.

  • Stainless steel blade barbed rope material is produced according to stainless steel plate and stainless steel wire, as a whole have achieved the purpose of high quality anticorrosion.

  • The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.