high quality fgd pump manufacturer

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

There is still some demand for galvanized barbed rope by daily residents, but often the quantity is not particularly much. If the barbed rope factory delivers goods, then the extra freight may be higher than the price of the customer to buy the barbed rope in the market. The thorn rope factory sells to customers who buy in large quantities. There is a lot of demand for it, and it also hopes to find a manufacturer to purchase. Customer procurement problems can be much more complete introduction in the thorn rope factory, but also let customers more at ease.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

Zinc is a silver-white metal, brittle at room temperature, soluble in acid can also be soluble in alkali, known as amphoteric metal. Pure zinc in dry air is more stable, in humid air or containing carbon dioxide and oxygen water is small, the surface will generate a layer of basic zinc carbonate based thin film layer, it can delay the corrosion rate of zinc layer. The corrosion resistance of zinc coating in aqueous solution of acid, alkali and sodium chloride is stronger.

1, zinc pot workers to resolutely do duty and responsibility. Do not leave the post without permission, always observe the change of steel wire galvanized layer, and according to the analysis of the results, master asbestos block gap friction need how long to press, replace the pressing face; Adjust the working face; Until the four faces of the asbestos block are used up, maintenance workers continue to use it after repair when necessary to reduce the consumption of asbestos block.

The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.