  • In order to remove the photosynovium and oxide remaining on the surface of galvanized iron wire after drawing or heat treatment, it is necessary to do the surface treatment of galvanized steel wire before plating. The common surface of low carbon steel wire is the light synovium or oxide of animal or vegetable oil; Medium and high carbon steel in addition to contain animal or vegetable oil components.

  • galvanized

  • The antisepsis of these materials is very different, the use of life is not the same. Cold galvanized cattle net, also known as electroplating, galvanized amount is small, rust in rain, but the price is cheap, the service life is 5-6 years. The amount of zinc on hot dip galvanizing (low zinc and high zinc) is about 60g to 400g, the service life is about 20-60 years, and the corrosion resistance is general.

  • Post time: 18-05-22

  • The barbed wire factory will store the blade barbed wire inventory in the appropriate place, because it understands the product characteristics.

  • To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the amount of surface-active substances brought in to Z. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

  • The production and processing process of blade barbed rope is tedious, which requires the cooperation of all departments, and the production cycle is relatively long. The barbed rope, whether galvanized barbed rope or stainless steel barbed rope, due to the relatively simple structure, the degree of mechanization in the production process is relatively high, so this is also a big difference in the price.

  • There is a good toughness and elasticity, in short, it can be easily made into a variety of shapes, and zinc as a coating is silver, very beautiful. This feature makes hot-dip galvanized wire handicrafts, wire mesh and other aspects are also used. Hot plating wire selection of high quality low carbon steel wire rod processing, is the selection of high quality low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes.

  • Pressure lock steel grid plate is at each intersection of bearing flat steel and horizontal bar, the horizontal bar is pressed into bearing flat steel or pre-slotted bearing flat steel through the pressure, the fixed steel grid plate, called pressure lock steel grid plate. The cross bar of the pressure lock steel grid plate is usually flat steel.

  • 1. After getting the bird cage, do not rush to use it. Clean the cage with a clean cloth or rubber. Then use fine yarn paper (do not use coarse sandpaper randomly), gently polish some parts that need to be polished again to improve the surface finish and trace, and pay attention to not damage the original bamboo green. After careful observation, use a razor blade to carefully clean the individual areas with small burrs.

  • Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

  • Because of its light weight, strength is relatively large has gradually begun to replace the original column. At the same time, due to the relatively uniform specifications, the barbed rope installation is also more beautiful. The direct spacing of the barbed rope is relatively fixed, which can effectively prevent crossing. At the same time, the mesh at the bottom is relatively dense, while the mesh at the top is relatively loose, which can save resources.

  • The wire rod should be normalized or soxhlet processed, instead of spheroidal annealing for standard large ones. Soxhlet process is widely used in the heat treatment of the center, especially the products before drawing. Avoid decarbonization during heat treatment. After heat treatment, sulfuric acid or hydrochloric acid pickling is used to remove iron sheet. The coating (see smooth carrier) can be dip-lime, phosphating, borax treatment or copper plating.

  • Post time: 07-02-23
  • After a long time of use, it will not rust like the corrosion layer on the surface of hot dip galvanized barbed rope, because the internal material of stainless steel barbed rope is the same as the material on the surface.

  • The application range of positive and negative twisted barbed wire is also very wide. It is a good choice for purchasing barbed wire. So what are the advantages of positive and negative twisted barbed wire compared with other barbed wires? The following  barbed wire factory will introduce the positive and negative twisted wire in detail. Three advantages of rope

  • 2, PVC coated barbed rope has strong corrosion and turbidity resistance
  • Great attention should be paid to pickling of large rolls of galvanized wire. Acid is highly corrosive. Therefore, when adding acid, the acid must be poured into the water, and it is along the wall of the cylinder, and not thrown down at once, so as not to cause splashing. Remember the order of acid pouring, acid into water rather than water into acid, water into acid will cause splashing and boiling, when pouring acid must wear protective glasses, beside must ensure that there are no non-professional people watching, so as not to cause some acid splashing danger.

  • After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

  • In GENERAL, THE HARDNESS OF A METAL IS OFTEN CONSIDERED AS THE RESISTANCE OF a MATERIAL TO COMPRESSION PLASTIC deformation, scratches, wear, or cutting. In the adjustment of zinc dip distance of galvanized wire, keep the original speed unchanged, according to the time of zinc dip, wire diameter, and then estimate the zinc dip distance. By adjusting the zinc dipping distance, the zinc dipping time of various specifications of steel wire is shortened by 5s on average compared with that before debugging, so that the zinc consumption is reduced, the zinc consumption per ton of steel wire is reduced from the original 61kg to 59.4kg.

  • Again: positive and negative twisting barbed rope appearance beautiful

  • 2. Eliminate the caked zinc residue at the zinc liquid surface

  • Post time: 17-11-22

  • Compared with traditional braided and twisted braided rope, the process of blade braided rope is relatively complex, and the price of raw materials is also relatively high.